In order to improve the high temperature strength of tungsten, 30~vol. pct ZrC particles were added to the tungsten matrix to form a 30ZrCp/W composite. The tensile properties from 20℃ to 1880℃ of the composite were examined. It was shown that with increasing testing temperature, the nonlinearity of the stress strain curve of 30ZrCp/W composite becames obvious over 1200℃ and the Young’s modulus decreases and the elongation increases. The ultimate tensile strength increases at first and then decreases with increasing testing temperature. The maximum strength of 431 MPa was obtained at 1000℃. The strengthening mechanism at high temperatures is the load transfer to ZrC particles and dislocation strengthening of the tungsten matrix with an effect of grain boundary strengthening.
关键词:
ZrCp/W composite
,
null
,
null
,
null
Yujin WANG
,
Yu ZHOU
,
Guiming SONG
,
Tingquan LEI
材料科学技术（英）
The elevated temperature mechanical properties of TiCp/W composites produced using powder metallurgical technique were investigated. Results show that with increasing temperature, the strength of TiCp/W composites increases gradually and reaches its maximum value at 1000℃, which is much higher than that at room temperature. The strengthening mechanisms at high temperature are attributed to dislocation strengthening and load transfer between matrix and particles.
关键词: